Product	Solvent	Solid (%)	VISCOSITY (25°C, cps)	COLOR	OH VALUE (mgKOH/g)	HYDROXYL CONTENT (%)	Speciality	Application
DSU 1250	XYL	50±2	Z₄-Z₅	<1	1-6	1.2	Fast drying; CAB / NC compatibility; good aluminum powder arrangement; high hardness.	Aluminum powder paint and color paint for household appliance plastics.
DSU 4270A	BAC	70±2	Y-Z₃	<1	5-9	4.2	High gloss, fullness and chemical resistance.	Topcoat and varnish, tank topcoat.
HE6625T	XYL/BAC/PMA	60	3,000-6,000	<1	4-10	1.5	Excellent aluminum powder arrangement; Good interlayer adhesion; Dry quickly.	It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for non-ferrous metal substrate coatings.
HE6628	XYL/BAC/PMA	60	3,500-7,000	<1	2-6	0.9	Excellent alignment of aluminum powder; Good adhesion to ABS, PS and metal substrates; Fast drying speed.	It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU plastic paint, hardware aluminum powder paint and pigmented coating. The coating can be sprayed on ABS and PS at one time.
HE6673	BAC/XYL	65	3,000-6,000	<1	5-10	3.0	High gloss, high fullness, good leveling property; Good weather resistance; Excellent chemical resistance.	It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU finish paint, automobile refinish paint and aluminum powder paint.
HE6775E	BAC	70	4,000-8,000	<1	6-12	3.0	High gloss, high solid content, high fullness, good leveling property; Good weather resistance, fast drying.	It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for PU cover varnish, pigmented paint and motorcycle paint, home appliance cover varnish.
HE6790	BAC	70	2,000-7,000	<1	5-9	4.5	High fullness, high gloss; Fast drying, high hardness; Excellent chemical resistance.	It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It has a high fullness and high gloss appearance, excellent mechanical properties and chemical resistance, excellent aging resistance, and high construction solid content, especially suitable for automotive coatings and motorcycle coatings.
DSU 7027B	BAC	70±2	Z₁-Z₃	<1	4-9	2.7	High gloss, weatherability and fullness.	Automotive repairing paint, PU varnish.